Product Details: Density(g/cm3) 1.405g/cm3 Hardness(HB) 270-280n/mm2 The highest continuous temperature( Celsius 110 Break down resistance(KV/mm) 18.6KV/mm Elastic modulus in tension(Gpa) 26.4-31Gpa Impact strength(nick) 8kg/m2 Tensile strength(Mpa) 70Mpa Bend strength(Mpa) 130-150Mpa…
UHMWPE Rods
Product Details: Density .93-0.94 g/cm3 Average molecular weight 4.0×10 g/mol Elongation art yield Less then 20 percent Tensile modulus 720 N/mm2 Wear by the sand-slurry method 100 mg (max) Vicat…
Cast Nylon Components
With the aid of advanced tools and equipment, we have been able to import Cast Nylon Components. For their outstanding characteristics like excellent wear & abrasion resistance and good load…
Nylon Rods
Product Details: Water absorption 0.8-1.0 percent Tensile Strength 760 kg/cm2 Hardness (Shore) 80-85 D Scale Melting Temp 225 degree centigrade Heat Resistance 100 degree centigrade Di-electrical strength 25 kv/mm Brand…
Polypropylene Sheets
Product Details: Density 0.905 gm/cm3 Tensile Strenght 330 kg/cm2 Elongation (Yield) 12 Percante Flexural Modulus 13,500 kg/cm2 Izod Impact Strength (Notched) 4.5 kg/cm Vicat Softening Point 152 degree centigrade Color…
Polyacetal Sheets
Product Details: Density 1.41-1.42 g/cm3 Tensile Strength at break 65 MPa Torsional Modulus 2600MPa Volume Resistivity 1015 ohm cm Surface Resistivity 2×1014 ohms Dielectric Strength (short time 2,3 mm) 32…
HM HDPE Sheets
Product Details: Density 0.95 g/cm3 Water absorption Less then 0.01 mg Tensile strength 3920 psi Elongation at yield 9 Percent Service Temprature(in air) -60 / +80 Degree Centigrade Thickness 1mm…
ABS Rods
Product Details: Diameter 8mm to 200mm Color Black Size Customized Ours is a trustworthy name in the business that brings forth a gigantic assemblage of ABS Rods that can be…
HDPE Sheets
Product Details: Density 0.95 g/cm3 Tensile Strength 4600 PSI Tensile Elongation at yield 900 Percent Hardness 69 Shore D Max operation Temperature 82 Degree Centigrade Size(FeetXFeet) Customized Thickness 1mm to…
Carbon Filled PTFE Components
Properties High Compressive Strength Better Wear Resistance Better Thermal Conductivity